White metal anchor corrosion on museum model


Recommended Posts

Recently visited the Mystic Seaport Museum in Mystic Connecticut and saw this superb model of Flying Fish. The cased model was excellent, great construction detail and rig. The unpainted model was aging very nicely, except for the anchors which were blooming with scale and deeply corroded. That old white metal corrosion again. In other cases I’ve seen painted anchor bursting like stuffed animals, white fuzz emerging from cracks in he paint caused by the expansion of the metal. In this case the corrosion looks like brownish orang bubles. The base under the Bow was discolored from material dripping off the anchors. Also two copper hull plates had come off. Oddly, the figure head appears fine, sugesting it’s made of stronger stuff. Real gold?

37639D89-87A7-48F4-9DBE-DCC77CA1D1E3.jpeg

A2B79E99-B514-40F2-BEF1-2C73372675D1.jpeg

9B727858-4777-44CF-B16A-701ECE654E23.jpeg

11D2D48B-F847-4D6E-999A-E7F0B79B29F3.jpeg

24744E85-43AC-4DF7-91BF-D67EBC646261.jpeg

1EAB48E7-8BB0-4A22-8D96-C1202972BF86.jpeg

Edited by JerseyCity Frankie

  

Quote

 

 Niagara USS Constitution 

 

Link to comment
Share on other sites

Corrosion could also be from lead as well as white metal. However, lead salts are more usually whiskery or powdery and white (lead carbonate).

Be sure to sign up for an epic Nelson/Trafalgar project if you would like to see it made into a TV series  http://trafalgar.tv

Link to comment
Share on other sites

  • 3 weeks later...
5 hours ago, wefalck said:

which speeds up corrosion in form of lead acetate

Welfalck,

 

That  little tidbit of formation worth a million dollars, thanks for posting.

John Allen

 

Current builds HMS Victory-Mamoli

On deck

USS Tecumseh, CSS Hunley scratch build, Double hull Polynesian canoe (Holakea) scratch build

 

Finished

Waka Taua Maori War Canoe, Armed Launch-Panart, Diligence English Revenue Cutter-Marine  Model Co. 


 

Link to comment
Share on other sites

Yep, I have a constitution with wonderful corroded anchors.  someday, I need to get the case off and replace the anchors, which are attached to the ratlines.  what a bummer!!  Thanks for showing what happens with this metal in an air tight case!  It's heart breaking to put all of that care into the build to see this happen to your model.

Edited by keelhauled
Link to comment
Share on other sites

Something else is also going as well, I see what looks like a drip spot from a liquid on the base wood surface. Could drastic swings in temperature cause moisture condensation on the anchor with enough buildup to drip over time?

I have also see this type of corrosion on parts using blackening agents and not being rinsed thoroughly with water after being treated. This usually starts in a hole or recess in a part.

Ken

Current build: Maersk Detroit"
Future builds:  Mamoli HMS Victory 1:90
Completed builds: US Brig Niagara, Dirty Dozen, USS Constitution, 18th Century Armed Longboat
https://modelshipworld.com/index.php?/topic/11935-uss-constitution-by-xken-model-shipways-scale-1768/

 

Link to comment
Share on other sites

  • 3 weeks later...

I had this unhappy event back in the 1980's with my Bluenose model. I had that powdery white dust all over the encased model. Two years ago I removed the affected elements, cleaned them up and repainted the one's I could salvage. They have yet to go back on the model as I was waiting to see if the problem would return. I have kept them inside a plastic case with no ill effects evident. To address the problem with the encased model I drilled 3 vent holes at the top of the back of the case and provided some venting in the case floor hidden by a name plate support. Since doing so I have had no sign of metal breakdown. I even installed a miniature muffin fan controlled by a timer to see if that would do the trick. It seemed to do the job.  So then I went completely to passive venting and that has worked as well. My case is glass on sides, front and top with mahogany framing. I have suspected the floor of the case might be part of the problem as it is mahogany plywood. They use formaldehyde in the plywood adhesive so watch out for that.

Joe

Link to comment
Share on other sites

Venting a case will help, but not necessarily eliminate the issue. Sealing lead-bearing metal parts before they deteriorate with something like clear nail varnish will also help, but is no guarantee against break-down over time. The most effective measures? Never use lead or white metal parts. Replace them with lead-free fittings and dispose of the originals using hazardous materials handling and at a suitable waste facility.

Be sure to sign up for an epic Nelson/Trafalgar project if you would like to see it made into a TV series  http://trafalgar.tv

Link to comment
Share on other sites

Druxey is right.

 My anchors were sealed with nail polish then painted with enamel (I didn't do this to seal the anchors for corrosion, but because I thought that the black enamel paint would be less likely to scratch to the metal during rigging).  The anchors split open with the corrosion.

Link to comment
Share on other sites

Without comment on whether the model (partially) in the photos is worthy of museum display, I'm surprised that a museum of Mystic Seaport's stature would display a model so obviously in need of conservation. Not only are the anchors corroding, but the copper bands on the stock are broken (perhaps by the expansion of the lead oxide beneath the stock halves,) but also there are rigging chains detached and hanging loose and staining on the base from apparent condensation. Not only have some copper plates come adrift, but the coppering and parts of the chains in the close-ups appears to have developed a green patina betraying that it has been stored in some time in an excessively humid environment.  Among curators, these are obvious problems that require prompt attention. Perhaps Mystic simply left it on display pending future-scheduled restoration.

 

If anyone is interested in what seems to be the "last word" on ship model lead corrosion, the USN NAVSEASYSCOM's research report is highly informative.  It can be found on line here: https://www.navsea.navy.mil/Home/Warfare-Centers/NSWC-Carderock/Resources/Curator-of-Navy-Ship-Models/Lead-Corrosion-in-Exhibition-Ship-Models/

 

 

 

Link to comment
Share on other sites

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

  • Recently Browsing   0 members

    • No registered users viewing this page.
×
×
  • Create New...