Dear all

I am about to laminate the stem and I would like your thoughts whether I could use PVA glue. The boat is 1:10 scale, there will be 14 laminates, each 0.5 mm thick and 20 mm wide. It will be a big stem!

I can use epoxy and I am sure it will come out fine with no spring back. However, working with epoxy is a dirty business, takes ages to dry and it will be a very hard stem, difficult to cut bevels etc.

Could I use PVA? Will there be appreciable spring back, glue starved areas, will the short opening time be a problem and will it be strong enough?

 

Vaddoc

Posted

I have seen PVA and Super glue used at the same time one to hold the joint at the start and the second to give you time A drop of SG in-between splashes of PVA 

Andy

Current Build

HM Granado CC

Past builds

 HMS Chatham CC, HM Convulsion CC,  Duke William German Kit, Fair American LSS, The Wright Flyer MS

Posted

I have done laminating with epoxy many times and rarely had any problems.  As for clean up I use mineral sirits for clean up.  The advantage once cured is stability and durablility. Carpenters glue is just as messy but also easy clean up..  However doe drying timor curing I have usually gone for a 24 hr rate to ensure proper adhesion.

David B

Join the conversation

You can post now and register later. If you have an account, sign in now to post with your account.

Guest
Reply to this topic...

×   Pasted as rich text.   Paste as plain text instead

  Only 75 emoji are allowed.

×   Your link has been automatically embedded.   Display as a link instead

×   Your previous content has been restored.   Clear editor

×   You cannot paste images directly. Upload or insert images from URL.

  • Recently Browsing   0 members

    • No registered users viewing this page.
×
×
  • Create New...